MATERIAL LIBRARY
Compare corrosion, magnetism and processing
Browse 18 stainless steels materials. Compare reference properties, product condition and processing notes, then open the interactive material library.
Filter, sort and compare materials →These are the same editorial reference ranges used by the material library, not certified product values. Match product form, temper, thickness, temperature and test direction. Do not enter a tensile-strength range directly as an allowable stress. Use an applicable qualified material condition in the calculator and choose a safety factor for the design criteria.
Martensitic stainless casting grade specified with quenching and tempering conditions.
Selected major-element mass-percent bands from published investment-casting references, independently organised; not a full composition table, strength input or certification to all current JIS/order conditions.
Investment casting (lost wax) / Secondary machining of specified faces and holes
Austenitic stainless casting grade; related to the SUS304 family but specified as cast steel.
Selected major-element mass-percent bands from published investment-casting references, independently organised; not a full composition table, strength input or certification to all current JIS/order conditions.
Investment casting (lost wax) / Secondary machining of specified faces and holes
Mo-containing austenitic stainless casting grade selected for the actual corrosion environment.
Selected major-element mass-percent bands from published investment-casting references, independently organised; not a full composition table, strength input or certification to all current JIS/order conditions.
Investment casting (lost wax) / Secondary machining of specified faces and holes
Precipitation-hardening stainless casting grade; solution and ageing conditions determine strength.
Selected major-element mass-percent bands from published investment-casting references, independently organised; not a full composition table, strength input or certification to all current JIS/order conditions.
Investment casting (lost wax) / Secondary machining of specified faces and holes
冷間加工で高いばね強度を得やすく、薄板ばね、クリップ、端子に使います。加工度、曲げ方向、スプリングバックを指定します。
純度、調質、製品形状、加工率、温度で特性が変わるため、採用品の証明書とデータシートを確認
密度: 7.9–8 g/cm³ · 縦弾性係数: 185–200 GPa
密度：室温の代表範囲。成分と温度で変化
縦弾性係数：室温の代表範囲。方向と温度で変化
打抜き・曲げ：調質と曲げ方向を管理 / スポット溶接：可能 / 切削：加工硬化に注意 / 不動態化・電解研磨
More machinable than SUS304, with relatively lower corrosion resistance and weldability.
Reference for machined stock; note cold-work condition
Density: 7.93 g/cm³ · Young's modulus: 190–200 GPa
Density：Reference
Young's modulus：Typical room-temperature range for austenitic stainless steel
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
Widely used stainless with balanced corrosion resistance, formability and availability.
Published typical properties; vary with cold work and temperature
Density: 7.93 g/cm³ · Young's modulus: 193 GPa
Density：Published typical
Young's modulus：Published typical
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
SUS304を低炭素化して溶接熱影響部の鋭敏化を抑えた材料で、溶接タンクや配管に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.9–8 g/cm³ · Tensile strength: 480–620 MPa · 0.2% proof stress: 175–260 MPa · Young's modulus: 190–200 GPa
Density：Typical range
Tensile strength：Reference range for solution-treated product forms
0.2% proof stress：Varies by product form and thickness
Young's modulus：Typical range near room temperature
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
高Cr・Niで耐熱性に優れ、炉部品や高温治具に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.9–8 g/cm³ · Tensile strength: 520–750 MPa · 0.2% proof stress: 205–300 MPa · Young's modulus: 190–200 GPa
Density：Typical range
Tensile strength：Reference range across solution-treated and worked conditions
0.2% proof stress：Varies by thickness and product condition
Young's modulus：Typical range near room temperature
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
Mo添加によりSUS304より孔食・すきま腐食への抵抗を高め、薬液・沿岸・食品装置に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.95–8.05 g/cm³ · Tensile strength: 520–700 MPa · 0.2% proof stress: 205–300 MPa · Young's modulus: 190–200 GPa
Density：Typical range
Tensile strength：Reference range for solution-treated product forms
0.2% proof stress：Varies by product form and thickness
Young's modulus：Typical range near room temperature
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
Mo improves corrosion resistance over SUS304; low carbon limits weld sensitisation.
Verify by product form, heat treatment and environment
Density: 7.98 g/cm³ · Tensile strength: 480–620 MPa · Young's modulus: 190–200 GPa
Density：Reference
Tensile strength：General reference range for solution-treated material
Young's modulus：Typical room-temperature range for austenitic stainless steel
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
Tiで炭化物を安定化し、溶接や高温履歴での粒界腐食を抑えます。高温配管、排気、熱交換部品に使います。
純度、調質、製品形状、加工率、温度で特性が変わるため、採用品の証明書とデータシートを確認
密度: 7.9–8 g/cm³ · 縦弾性係数: 190–200 GPa
密度：室温の代表範囲。成分と温度で変化
縦弾性係数：室温の代表範囲。方向と温度で変化
切削：加工硬化に注意 / 曲げ・絞り：可能 / TIG溶接：適合溶加材と清浄度を管理 / 酸洗・不動態化
オーステナイト相とフェライト相を持ち、高強度と耐孔食性を生かして海水・薬液・圧力機器に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.7–7.9 g/cm³ · Tensile strength: 620–850 MPa · 0.2% proof stress: 450–650 MPa · Young's modulus: 195–205 GPa
Density：Typical range
Tensile strength：Reference range for solution-treated product forms
0.2% proof stress：Varies by product form and thermal history
Young's modulus：Typical range near room temperature
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
焼入れ可能な13Cr系で、強度・耐摩耗と中程度の耐食性を組み合わせます。軸、バルブ、刃物、機械部品に使います。
純度、調質、製品形状、加工率、温度で特性が変わるため、採用品の証明書とデータシートを確認
密度: 7.7–7.8 g/cm³ · 縦弾性係数: 195–205 GPa
密度：室温の代表範囲。成分と温度で変化
縦弾性係数：室温の代表範囲。方向と温度で変化
切削：焼なまし状態で行う / 研削：焼けと割れを管理 / 溶接：予熱・後熱を検討 / 焼入れ・焼戻し
焼入れで高硬度が得られ、シャフト、刃物、金型部品に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.7–7.8 g/cm³ · Tensile strength: 650–850 MPa · Young's modulus: 195–205 GPa
Density：Typical range
Tensile strength：Reference range across annealed and treated conditions
Young's modulus：Typical range
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
Magnetic general-purpose ferritic grade with little nickel; check corrosion by environment.
Verify by product form and finish
Density: 7.7 g/cm³ · Young's modulus: 195–205 GPa
Density：Reference
Young's modulus：Typical room-temperature range for ferritic stainless steel
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
ステンレスの中でも高硬度で、軸受、刃物、精密部品に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.6–7.7 g/cm³ · Tensile strength: 760–2000 MPa · Young's modulus: 195–205 GPa
Density：Typical range
Tensile strength：Very broad range from annealed to hardened and tempered material
Young's modulus：Typical range
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing
耐食性と高強度を両立し、軸、バルブ、航空・装置部品に使います。
Reference range; verify the product standard, condition, grade and maker datasheet.
Density: 7.7–7.9 g/cm³ · Tensile strength: 930–1310 MPa · 0.2% proof stress: 725–1175 MPa · Young's modulus: 190–200 GPa
Density：Typical range
Tensile strength：Reference range across H900–H1150-class conditions
0.2% proof stress：Strongly dependent on ageing condition
Young's modulus：Typical range
Machining / Bending / sheet-metal work / TIG / laser welding / Laser / shearing